The effect of immediate dentin sealing and optical powder removal method on the fracture resistance of CAD/CAM-fabricated endocrowns
El-Damanhoury, H.M.; Gaintantzopoulou, M.
International Journal of Computerized Dentistry 19(2): 135-151
2016
ISSN/ISBN: 1463-4201 PMID: 27274562 Document Number: 686754
To evaluate the effect of immediate dentin sealing and optical powder removal method on the fracture resistance of CAD/CAM-fabricated ceramic endocrowns. Seventy-eight extracted premolars were endodontically treated. Standardized endocrown preparations were done in 60 teeth. Teeth were divided equally (n = 10) depending on the treatment of dentin (delayed sealing [DS] or immediate sealing [IS]), and the methods of optical powder removal (air-water spray washing [AW]; microabrasion [MA]; or aqueous suspension of pumice [PB], followed by air-water spray washing). After cementation, specimens were thermocycled (5,000 cycles, 5°C/50°C) and stored in distilled water for 1 week. Specimens were loaded in compression using a universal testing machine until failure. Failure load was recorded, and modes of failure were examined under a stereomicroscope. Micromorphological evaluation of different dentin treatments was done under SEM (n = 3). Results were analyzed using two-way ANOVA and Bonferroni post hoc multiple comparison tests (α = 0.05). Fracture resistance of all IS groups was significantly lower than DS groups, except for AW. There was no statistically significant difference between powder removal methods. Immediate dentin sealing does not improve the fracture resistance of endocrown restorations. Air-water spray washing is adequate to remove the optical powder after optical scanning impression taking.