Treatment of dental root fracture by medium energy CO2 laser and DP-bioactive glass paste. Part. II: Compositional, structure, and phase changes of DP-bioglass paste after exposed to CO2 laser
Tseng, Y.C.; Lin, F.H.; Lin, C.P.; Lan, W.H.; Liao, J.D.
Biomedical Sciences Instrumentation 35: 285-290
1999
ISSN/ISBN: 0067-8856 PMID: 11143363 Document Number: 506826
Fractured teeth are difficult to treat effectively. Currently, such as root fractures are usually treated by full-coverage restoration, root amputation, or tooth extraction. If the fusion of tooth fracture by laser were possible, it could offer a different therapy to repair fracture teeth. We tried to use a developed DP-bioactive glass paste to fuse or bridge the tooth crack line by a medium energy continuous-wave CO2 laser. The present report was focused on the phase transformation and rescrystallization of DP-bioactive paste during expose to the CO2 laser. The materials will examine by means of XRD, FTIR, DTA/TGA, and SEM. From the study, we could expect that the temperature increase due to laser irradiation must be over than 900 degrees C and the DP-bioactive glass paste could be melted in a short period of time after irradiation. In the study, we successfully developed a DP-bioactive glass paste which could form a melting glass within minutes after exposed to a medium energy density continuous-wave CO2 laser. The paste will be used to bridge the enamel or dentine surface crack by the continuous-wave CO2 laser in the near future.